| 3/16" | 1/4" | 5/16" | 3/8" | 7/16" | 1/2" |
|---|---|---|---|---|---|
| 4.8mm | 6.3mm | 7.9mm | 9.5mm | 11.1mm | 12.7mm |
| 9/16"" | 5/8"" | 3/4"" | 7/8"" | 1"" | 1 1/8"" |
| 4.8mm | 15.9mm | 19mm | 22.2mm | 25.4mm | 28.6mm |
| 1 1/4"" | 1 3/8"" | 1 1/2"" | 1 5/8"" | 1 3/4"" | 2"" |
| 31.8mm | 34.9mm | 38.1mm | 41.3mm | 44.5mm | 50.8mm |
| 2 1/4"" | 2 1/2"" | 2 3/4"" | 3"" | 3 1/4"" | 3 1/2"" |
| 57.2mm | 63.5mm | 69.9mm | 76.2mm | 82.6mm | 88.9mm |
| 3 3/4"" | 4"" | 4 1/4"" | 4 1/2"" | 4 3/4"" | 5"" |
| 95.3mm | 101.6mm | 108mm | 114.3mm | 120.7mm | 127mm |
| 5 1/4"" | 5 1/2"" | 5 3/4"" | 6"" | ||
| 133.4mm | 139.7mm | 146.1mm | 152.4mm |
Alloy 304/304L (UNS S30400/S30403) is the most widely utilized “18-8” chromium-nickel austenitic stainless steel. It is an economical and versatile corrosion resistant alloy suitable for a wide range of general purpose applications.
It is common practice for 304L to be dual certified as 304 and 304L. The low carbon chemistry of 304L combined with an addition of nitrogen enables 304L to meet the mechanical properties of 304.
Alloy 304/304L resists atmospheric corrosion, as well as, moderately oxidizing and reducing environments. The alloy has excellent resistance to intergranular corrosion in the as-welded condition. Alloy 304/304L has excellent strength and toughness at cryogenic temperatures.
Alloy 304/304L is non-magnetic in the annealed condition, but can become slightly magnetic as a result of cold working or welding. It can be easily welded and processed by standard shop fabrication practices.
Applications
Chemical and Petrochemical
Processing—pressure vessels, tanks, heat exchangers, piping systems, flanges, fittings, valves and pumps
Food and Beverage Processing
Medical
Mining
Petroleum Refining
Pharmaceutical Processing
Power Generation—nuclear
Pulp and Paper
Standards
ASTM........A 240
ASME........SA 240
AMS..........5511/5513
QQ-S........766
Corrosion Resistance
Alloy 304/304L has good resistance to atmospheric corrosion, foods and beverages and to many organic and inorganic chemicals in moderately oxidizing to moderately reducing environments. The high chromium content of the alloy provides resistance to oxidizing solutions such as nitric acid up to 55% weight and up to 176°F (80°C).
Alloy 304/304L also resists moderately aggressive organic acids such as acetic. The nickel present in the alloy provides resistance to moderately reducing solutions such as pure phosphoric acid, whatever the concentration, in cold solutions and up to 10% diluted hot solutions. The alloy can also operate successfully in caustic solutions free of chlorides or Alloy 304/304L does not perform well in more highly reducing environments such as those containing chlorides and sulfuric acid.
Alloy 304/304L performs well in fresh water service with low levels of chlorides (less than 100ppm). At higher chloride levels the grade is susceptible to crevice corrosion and pitting. For successful performance under these more severe conditions, higher molybdenum content is need such as 316/316L. Alloy 304/304L is not recommended for service in marine environments.
In most instances, the corrosion resistance of Alloys 304, 304L and 304H will be roughly equal in most corrosive environments. However, in environments that are sufficiently corrosive to cause intergranular corrosion of welds and heat-affected zones Alloy 304L should be used because of its low carbon content.